I am thinking i will weld this in a can. Forge all the material I am going to use flat then stack and seal it up. This way i can do a nice long soak and it should weld up nice without any flux. Then upon re-weld I will MIG all the seams up to create a sealed unit again and dry weld it. I will take my time on this one. Even if this does not make the best knife blade material it will be a part of history.
|